• Energy Research

Industrial valorisation of low cost and renewable biomass as raw precursor of activated carbon for environmental applications is an interesting alternative to costly commercial activated carbons. In this study, the possible use of Mediterranean, Posidonia oceanica fibrous biomass, as a precursor for chars and physically activated carbons, is investigated. Firstly, the raw marine material was chemically and biochemically characterised throughout dry-basis elemental, X-ray photoelectron spectroscopy (XPS) and scanning electron microscopy (SEM) analysis. Then, several P. oceanica chars were prepared and characterised under different pyrolysis times and temperatures. In addition, physically activated carbons (PACs) were produced via water steam flow under various activation periods. The results showed that the pyrolysis induces the creation of pores at different levels with respect to the involved temperature. Thereafter, the physical activation tends to enhance the development of the porous structure. In that issue, the performed Brunauer-Emmett-Teller (BET) and Barrett-Joiner-Halenda (BJH) analysis revealed that the prepared PACs have a mainly mesoporous inner morphology with a varying fraction of micropores.

Since 2011, substantial amounts of pelagic Sargassum algae have washed up along the Caribbean beaches and the Gulf of Mexico, leading to negative impacts on the economy and the environment of those areas. Hence, it is now crucial to develop strategies to mitigate this problem while valorizing such invasive biomass. This work deals with the successful exploitation of this pelagic Sargassum seaweed for the fabrication of carbon materials that can be used as electrodes for supercapacitors. Pelagic Sargassum precursors were simply pyrolyzed at temperatures varying from 600 to 900 °C. The resultant carbonaceous materials were then extensively characterized using different techniques, such as nitrogen adsorption for textural characterization, as well as X-ray photoelectron (XPS), Fourier transform infrared spectroscopies (FT-IR) and scanning electron microscopy (SEM), to understand their structures and functionalities. The electrochemical properties of the carbon materials were also tested for their performance as supercapacitors using cyclic voltammetry (CV), the galvanostatic method and electrochemical impedance spectroscopy analyses (EIS). We managed to have a large specific surface, i.e., 1664 m2 g−1 for biochar prepared at 800 °C (CS800). Eventually, CS800 turned out to exhibit the highest capacitance (96 F g−1) over the four samples, along with the highest specific surface (1664 m2 g−1), with specific resistance of about 0.07 Ω g −1.

Turbinaria turbinata brown seaweeds were tested as carbon electrode material in symmetric, electrochemical supercapacitors. The electrochemical properties of the carbon materials were characterised for their application as supercapacitors using cyclic voltammetry, galvanostatic charge/discharge method and electrochemical impedance spectroscopic analyses. Our initial results showed that the optimal behaviour was obtained for the sample prepared by pyrolysis at 800 °C. The average surface area of the carbon was 812 m2/g. Electrochemical tests with an organic electrolyte gave the following interesting results: a capacitance of 74.5 F/g, a specific series resistance of 0.5 Ω cm2 and an ionic resistivity of 1.3 Ω cm2. These results show the promising capacitive properties of carbon derived from seaweeds and their application in electrochemical supercapacitors.