Solid-state Li-ion conductors are of broad interest in electrochemical energy storage, especially in solid-state Li batteries that serve as a promising alternative for the next-generation safe and high-energy-density batteries. Exploring solid-state superionic conductors is significant for the development of solid-state Li batteries with high performance. Herein, we report a disordered rock-salt (A 1 B 1 )-structured solid electrolyte (Li 0.625 Al 0.125 H 0.25 )­(Cl 0.75 O 0.25 ) (abbr. LAHCO) that was synthesized using Li 2 OHCl and LiAlCl 4 as precursors. Neutron diffraction reveals that Li, Al, and H atoms occupy the A sites and O and Cl atoms occupy the B sites in the A 1 B 1 structure for pure LAHCO. The LAHCO compound with excess LiAlCl 4 shows the highest Li + ionic conductivity of ∼10 –4 S cm –1 at room temperature due to the disordering induced by configurational entropy as well as the entropy of mixing. Moreover, LAHCO–LiAlCl 4 solid electrolyte exhibits a stable polarization voltage under a current density of 5–50 μA cm –2 in Li symmetric cells. This work not only explicates the importance of Li-ion conductors with a rock-salt structure but also contributes toward the development of solid-state Li-ion conductors for broad applications.