Nail polish, in particular gel nail polish, is the most used cosmetic product. The components of the gel polish, which determine both toxicity and consumer color properties, are pigments. Zn-Al layered double hydroxides intercalated with anionic food dyes are promising pigments for use in gel polish. The parameters of the samples of Orange Yellow S-intercalated Zn-Al (Zn:Al=4:1 and Zn:Al=2:1) hydroxides synthesized at pH=8 and pH=11 were studied. The crystal structure of the samples was studied by X-ray phase analysis and thermogravimetry, and the pigment properties – by the method of measuring and calculating color characteristics in the CIELab and XYZ systems. The color characteristics of gel nail polish samples prepared using synthesized pigments were studied in a similar way. X-ray phase analysis and thermogravimetry showed that Zn-Al-Orange Yellow S pigments synthesized at both Zn:Al ratios and pH were layered double hydroxides with the α-Zn(OH) 2 structure. The phenomenon of the decomposition of Zn-Al LDH to ZnO during the synthesis was revealed. As a result, all Zn-Al-Orange Yellow S pigment samples contained both layered double hydroxide and zinc oxide. It was shown that all samples of the Zn-Al-Orange Yellow S pigment obtained at pH 8 and 11 and the ratios Zn:Al=4:1 and Zn:Al=2:1 had high pigment characteristics and are promising for use in gel polish. The samples of gel nail polish with synthesized pigments have a red-orange color (сolor tone 595–604 nm) with high monochromaticity (color purity 63–75 %) and color saturation (48.7–58.3)