• Energy Research

Red mud-based inorganic polymer spheres were used as alternative pH regulators and process enhancers in sequencing batch anaerobic reactors treating cheese whey. This byproduct tends to quickly acidify under anaerobic conditions, and the common route to control pH and ensure suitable conditions for methane production involves the use of commercial alkaline raw materials. The spheres were synthesized using significant amounts of hazardous and toxic waste, red mud (50 wt% of solid components), whose recycling is challenging. The inorganic polymeric spheres, when compared to virgin alkaline raw materials, improved organic matter removal by 44%, prevented VFA accumulation (acidification degree less than 20%), maintained pH values in a range (6.5-7.2) to ensure maximum methanogenic activity by archaea microorganisms, and boosted the methane volume by ~90%. These promising results demonstrate the feasibility and performance advantages of using these innovative spheres instead of virgin raw materials, which is an important tool towards sustainable development.

Red mud-based inorganic polymer spheres were used as alternative pH regulators and process enhancers in sequencing batch anaerobic reactors treating cheese whey. This byproduct tends to quickly acidify under anaerobic conditions, and the common route to control pH and ensure suitable conditions for methane production involves the use of commercial alkaline raw materials. The spheres were synthesized using significant amounts of hazardous and toxic waste, red mud (50 wt% of solid components), whose recycling is challenging. The inorganic polymeric spheres, when compared to virgin alkaline raw materials, improved organic matter removal by 44%, prevented VFA accumulation (acidification degree less than 20%), maintained pH values in a range (6.5-7.2) to ensure maximum methanogenic activity by archaea microorganisms, and boosted the methane volume by ~90%. These promising results demonstrate the feasibility and performance advantages of using these innovative spheres instead of virgin raw materials, which is an important tool towards sustainable development.

The immobilization of hazardous wastes in ordinary Portland cement (OPC)-based materials has been widely studied and implemented. OPC-based materials have a high carbon footprint associated with their production and geopolymer materials are a sustainable and eco-friendly alternative. Therefore, this work aimed to immobilize two hazardous industrial wastes: copper wastewater sludge and phosphogypsum in one-part geopolymer materials. For that purpose, the precursor was partially substituted by these wastes (5, 10 and 20 wt.%) in the formulations. The geopolymer fresh and hardened state properties were evaluated, and the immobilisation of pollutants was determined through leaching tests. In phosphogypsum pastes (PG5, PG10 and PG20) it was observed that the compressive strength decreased with the increase in its amount, varying between 67 MPa and 19 MPa. In copper sludge pastes, the compressive strength of the specimens (CWS5 and CWS10) reached ~50 MPa. The mortars, MPG10 and MCWSs10, had compressive strengths of 13 MPa and 21 MPa, respectively. Leaching tests showed that pastes and mortars immobilise the hazardous species of the wastes, except for As from copper sludge, whose the best result was found in the compact paste (CWSs10) that leached 2 mg/kg of As. Results suggest that optimized compositions are suitable for the construction sector.

The immobilization of hazardous wastes in ordinary Portland cement (OPC)-based materials has been widely studied and implemented. OPC-based materials have a high carbon footprint associated with their production and geopolymer materials are a sustainable and eco-friendly alternative. Therefore, this work aimed to immobilize two hazardous industrial wastes: copper wastewater sludge and phosphogypsum in one-part geopolymer materials. For that purpose, the precursor was partially substituted by these wastes (5, 10 and 20 wt.%) in the formulations. The geopolymer fresh and hardened state properties were evaluated, and the immobilisation of pollutants was determined through leaching tests. In phosphogypsum pastes (PG5, PG10 and PG20) it was observed that the compressive strength decreased with the increase in its amount, varying between 67 MPa and 19 MPa. In copper sludge pastes, the compressive strength of the specimens (CWS5 and CWS10) reached ~50 MPa. The mortars, MPG10 and MCWSs10, had compressive strengths of 13 MPa and 21 MPa, respectively. Leaching tests showed that pastes and mortars immobilise the hazardous species of the wastes, except for As from copper sludge, whose the best result was found in the compact paste (CWSs10) that leached 2 mg/kg of As. Results suggest that optimized compositions are suitable for the construction sector.

Electroplating sludge (ES) is currently disposed in landfills and, because of its heavy metal content, poses serious threats to the environment and human health. However, ES might have potential use as colouring agent due to its high concentration of chromium and nickel. Thus, the present work aims at studying the effect of ES incorporation into stoneware bodies. The influence on the final characteristics of fired samples, ES amount and pre-treatment were analysed. It was found that stoneware pastes having uniform brownish hues can be obtained with only 3 wt.% of sieved (<212 μm) ES. The obtained specimens have, once fired, the desired technical and aesthetical characteristics. Further, leaching tests confirmed the immobilisation of hazardous ES species in the ceramic matrix. Hence, it can be concluded that this waste can be used as colouring agent of stoneware pastes substituting commercial pigments and contributing to more sustainable consumption and production in the ceramic sector.

Electroplating sludge (ES) is currently disposed in landfills and, because of its heavy metal content, poses serious threats to the environment and human health. However, ES might have potential use as colouring agent due to its high concentration of chromium and nickel. Thus, the present work aims at studying the effect of ES incorporation into stoneware bodies. The influence on the final characteristics of fired samples, ES amount and pre-treatment were analysed. It was found that stoneware pastes having uniform brownish hues can be obtained with only 3 wt.% of sieved (<212 μm) ES. The obtained specimens have, once fired, the desired technical and aesthetical characteristics. Further, leaching tests confirmed the immobilisation of hazardous ES species in the ceramic matrix. Hence, it can be concluded that this waste can be used as colouring agent of stoneware pastes substituting commercial pigments and contributing to more sustainable consumption and production in the ceramic sector.

The production of paper pulp by the Kraft method generates considerable amounts of wastes. Namely, lime mud generated in the recovery circuit of chemical reagents, biological sludge from the wastewater treatment of wood digestion process and fly ash collected in the fluidized bed combustor used to generate electricity from biomass burning. The final destination of such wastes is an important concern, since environmental regulations are becoming stricter regarding their landfill. Driven by this fact, industries are looking for more sustainable solutions, such as the recycling in distinct products. This work tested these wastes as secondary raw materials to produce clinker/cement that was then experienced in mortar formulations. The first step involved the residues detailed characterization and a generated amounts survey. Then, specific but simple steps were suggested, aiming to facilitate transport and manipulation. Distinct blends were prepared and fired in order to get belitic and Portland clinkers. The Portland clinkers were processed at lower temperatures than the normally used in the industry due to the presence of mineralizing impurities in some wastes. Belite-based cements were used to produce mortars that developed satisfactory mechanical strength and did not reveal signs of deterioration or durability weaknesses.